SECO Grade A-E Binderless Borosilicate Glass Microfiber Filter Media, 3.7 cm dia
Filter Media, 3.7 cm dia, Borosilicate Glass Microfiber, Grade A-E, Binderless, 0.33 mm Thickness, 1 µm Particle Retention, 60 g/m2 Nominal Basis Weight, 15 sec Filtration Speed, 500°C Max. Temperature
- Manufacturer Part No: AE3700
- SECO Part No: IWT-AE3700
- Sold As:
-
Availability:
Login to View Your Price
-
List Price :
Glass microfiber filters offered in this product range are produced from 100% borosilicate glass microfiber without the use of binders or strengthening agents. These filters offer many advantages in a wide range of analytical applications. The fibers used to manufacture these depth filters are smooth and uniform. This permits their characteristically high flow rates while allowing retention of exceptionally small particles and high load capacity. These characteristics are particularly important in applications involving high concentrations of particulate or gelatinous substances. In choosing the appropriate filter for a specific application, careful consideration should be given to the physical form and concentration of the material to be captured by the filter. Fine porosity and fast flow rate, with a 1 µm size particle retention. Binderless borosilicate glass microfiber. DOP efficiency is 99.98%. Primarily used in suspended solids and air monitoring.
| Diameter | : | 3.7 cm |
| Grade | : | Grade A-E |
| Material (ml/min) | : | Borosilicate Glass Microfiber |
| Binder Type | : | Binderless |
| Maximum Temperature | : | 500°C |
| Nominal Basis Weight | : | 60 g/m2 |
| Particle Retention in Liquid | : | 1 µm |
| Shape | : | Die-cut |
| Thickness | : | 0.33 mm |
| Filtration Speed | : | 15 sec |
| Pore Size | : | 3.6 µm |
- Fastest flow rate
- High load capacity
- Retention of particles to sub-micron size
- Use in liquid and gaseous filtration
- Inert fiber composition
- Free of binders or additives